ExxonMobil Escorene® LD-141 EVA Shrink Film Resin, FMI

ExxonMobil Escorene® LD-141 EVA Shrink Film Resin, FMI 物性表: ExxonMobil Escorene® LD-141 EVA Shrink Film Resin, FMI物性表及特性介绍,ExxonMobil Escorene® LD-141 EVA Shrink Film Resin, FMI注塑参数详情,如需ExxonMobil Escorene® LD-141 EVA Shrink Film Resin, FMI下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 0.3
  • 密度 [g/cm3]: 0.923
 
Physical PropertiesMetricEnglishComments
Density 0.923 g/cc0.0333 lb/in³Exxon Method
Thickness 76.2 microns3.00 mil
Melt Flow 0.30 g/10 min0.30 g/10 minExxon Method
 
Mechanical PropertiesMetricEnglishComments
Film Tensile Strength at Yield, MD 8.90 MPa1290 psiASTM D882
Film Tensile Strength at Yield, TD 8.20 MPa1190 psiASTM D882
Film Elongation at Break, MD 200 %200 %ASTM D882
Film Elongation at Break, TD 500 %500 %ASTM D882
Secant Modulus, MD 0.152 GPa22.0 ksiASTM D882
Secant Modulus, TD 0.193 GPa28.0 ksiASTM D882
Elmendorf Tear Strength MD 100 g100 gASTM D1922
Elmendorf Tear Strength TD 200 g200 gASTM D1922
Elmendorf Tear Strength, MD 1.30 g/micron33.0 g/milASTM D1922
Elmendorf Tear Strength, TD 2.64 g/micron67.0 g/milASTM D1922
Dart Drop 3.94 g/micron100 g/milF50; ASTM D1709
Dart drop Test 300 g0.662 lbF50; ASTM D-1709
Film Tensile Strength at Break, MD 22.0 MPa3190 psiASTM D882
Film Tensile Strength at Break, TD 21.0 MPa3050 psiASTM D882
 
Thermal PropertiesMetricEnglishComments
Melting Point 107 °C225 °FExxon Method
 
Optical PropertiesMetricEnglishComments
Haze 20 %20 %ASTM D1003
Gloss 40 %40 %45°, ASTM D-2457

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-29656.html

免责声明: 本文 ExxonMobil Escorene® LD-141 EVA Shrink Film Resin, FMI 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4