- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 0.951
- 弯曲强度 [MPa]: 4.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | Exxon Method |
| Apparent Bulk Density | 0.577 g/cc | 0.0208 lb/in³ | ASTM D1895 (B) |
| Viscosity | 2000 cP @Temperature 121 °C | 2000 cP @Temperature 250 °F | melt viscosity; ASTM D-3236 |
| Melt Flow | 25 g/10 min | 25 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 4.80 MPa | 696 psi | ASTM D638 |
| Elongation at Break | 800 % | 800 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 69.0 °C | 156 °F | Exxon Method |
| Vicat Softening Point | 118 °C | 244 °F | Softening Point, R&B; ASTM E-28 |