- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.951
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 2.3 g/10 min | 2.3 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 3.00 MPa | 435 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 2.00 MPa | 290 psi | ASTM D882 |
| Film Elongation at Break, MD | 330 % | 330 % | ASTM D882 |
| Film Elongation at Break, TD | 640 % | 640 % | ASTM D882 |
| Secant Modulus, MD | 0.0300 GPa | 4.35 ksi | ASTM D882 |
| Secant Modulus, TD | 0.0400 GPa | 5.80 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 160 g | 160 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 30 g | 30 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 5.04 g/micron | 128 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 0.945 g/micron | 24.0 g/mil | ASTM D1922 |
| Dart Drop | 12.9 g/micron | 328 g/mil | F50; ASTM D1709 |
| Dart drop Test | 410 g | 0.904 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 75.0 °C | 167 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 1.5 % | 1.5 % | ASTM D1003 |
| Gloss | 80 % | 80 % | 45°, ASTM D-2457 |