- 熔体流动速率 [g/10min]: 1.3
- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 9.0
- 弯曲强度 [MPa]: 14.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D1505 |
Thickness | 25.4 microns | 1.00 mil | |
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 49 | 49 | ASTM D2240 |
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM D638 |
Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 |
Elongation at Break | 750 % | 750 % | ASTM D638 |
Modulus of Elasticity | 0.220 GPa | 31.9 ksi | Secant; ASTM D638 |
Secant Modulus, MD | 0.130 GPa | 18.9 ksi | ASTM D882 |
Secant Modulus, TD | 0.145 GPa | 21.0 ksi | ASTM D882 |
Dart Drop | 7.28 g/micron | 185 g/mil | ASTM D1709 |
Dart drop Test | 185 g | 0.408 lb | ASTM D1709 |
Film Tensile Strength at Break, MD | 19.0 MPa | 2760 psi | ASTM D882 |
Film Tensile Strength at Break, TD | 18.0 MPa | 2610 psi | ASTM D882 |
Thermal Properties | Metric | English | Comments |
Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 |
Optical Properties | Metric | English | Comments |
Haze | 4.5 % | 4.5 % | ASTM D1003 |
Gloss | 75 % | 75 % | at 45°; ASTM D523 |
Processing Properties | Metric | English | Comments |
Melt Temperature | 177 - 188 °C | 351 - 370 °F |