- 熔体流动速率 [g/10min]: 1.2
- 密度 [g/cm3]: 0.928
- 拉伸强度 [MPa]: 8.0
- 弯曲强度 [MPa]: 16.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 g/cc | 0.0335 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.2 g/10 min | 1.2 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 44 | 44 | ASTM D2240 |
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D638 |
| Film Elongation at Break, MD | 250 % | 250 % | ASTM D882 |
| Film Elongation at Break, TD | 400 % | 400 % | ASTM D882 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Modulus of Elasticity | 0.138 GPa | 20.0 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.104 GPa | 15.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.110 GPa | 16.0 ksi | ASTM D882 |
| Dart Drop | 11.0 g/micron | 280 g/mil | ASTM D1709 |
| Dart drop Test | 280 g | 0.617 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Gloss | 70 % | 70 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 193 - 204 °C | 379 - 399 °F | |