- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D1505 | ||
| Particle Size | >= 150 µm | >= 150 µm | pan, 7% | ||
| <= 500 µm | <= 500 µm | sieve < 5% | |||
| Vinyl Acetate Content | 20 % | 20 % | wt %; Exxon Mobil | ||
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 6.00 MPa | 870 psi | ASTM D638 | ||
| Elongation at Break | 240 % | 240 % | 50 mm/min; ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 83.0 °C | 181 °F | DSC; ASTM D3418 | ||
| 90.0 °C | 194 °F | fusing temperature | |||
| Vicat Softening Point | 49.0 °C | 120 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Max Dry Flow | max 37 sec/100g | ASTM | |||