- 熔体流动速率 [g/10min]: 1.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.929 g/cc | 0.929 g/cc | ISO 1183 |
| Vinyl Acetate Content | 9.0 % | 9.0 % | |
| Thickness | 40.0 microns | 1.57 mil | for samples tested on this data sheet |
| 25.0 - 300 microns | 0.984 - 11.8 mil | possible range, depending on extrusion conditions | |
| Melt Flow | 1.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 7.80 MPa | 1130 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 6.50 MPa | 943 psi | ISO 527-3 |
| Film Elongation at Break, MD | 370 % | 370 % | ISO 527-3 |
| Film Elongation at Break, TD | 600 % | 600 % | ISO 527-3 |
| Modulus of Elasticity | 0.110 GPa | 16.0 ksi | ISO 527-2 |
| Elmendorf Tear Strength, MD | 3.30 g/micron | 83.8 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 3.70 g/micron | 94.0 g/mil | ISO 6383-2 |
| Dart drop Test | 480 g | 1.06 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 98.0 °C | 208 °F | ISO 11357 |
| Vicat Softening Point | 82.0 °C | 180 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.5 % | 3.5 % | ISO 14782 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 - 180 °C | 302 - 356 °F | |