  4. Overview of materials for Acrylic, Impact Modified, Molded

Overview of materials for Acrylic, Impact Modified, Molded

Overview of materials for Acrylic, Impact Modified, Molded 物性表: Overview of materials for Acrylic, Impact Modified, Molded物性表及特性介绍,Overview of materials for Acrylic, Impact Modified, Molded注塑参数详情,如需Overview of materials for Acrylic, Impact Modified, Molded下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 0.7
  • 密度 [g/cm3]: 1.04
  • 吸水率 [%]: 0.1
  • 缺口冲击强度: 0.2
  • 拉伸强度 [MPa]: 28.0
  • 断裂伸长率 [%]: 41.2
  • 弯曲强度 [MPa]: 32.0
  • 弯曲模量 [MPa]: 1.36
  • 硬度: 61.0
  • 热变形温度 [℃]: 78.0
 
Physical PropertiesMetricEnglishComments
Density 1.04 - 1.19 g/cc0.0376 - 0.0430 lb/in³Average value: 1.15 g/cc Grade Count:125
Volatiles 1.00 %1.00 %Average value: 1.00 % Grade Count:6
Water Absorption 0.100 - 2.00 %0.100 - 2.00 %Average value: 0.366 % Grade Count:61
Moisture Absorption at Equilibrium 0.300 - 0.400 %0.300 - 0.400 %Average value: 0.360 % Grade Count:7
Water Absorption at Saturation 0.300 %0.300 %Average value: 0.300 % Grade Count:6
Particle Mesh Size 30.0 Mesh30.0 MeshAverage value: 30.0 Mesh Grade Count:6
Viscosity  975000 - 975000 cP
@Temperature 240 - 240 °C		975000 - 975000 cP
@Temperature 464 - 464 °F		Average value: 975000 cP Grade Count:1
 975000 - 975000 cP
@Shear Rate 100 - 100 1/s		975000 - 975000 cP
@Shear Rate 100 - 100 1/s		Average value: 975000 cP Grade Count:1
Linear Mold Shrinkage 0.00200 - 0.00800 cm/cm0.00200 - 0.00800 in/inAverage value: 0.00504 cm/cm Grade Count:104
Melt Flow 0.700 - 16.0 g/10 min0.700 - 16.0 g/10 minAverage value: 4.18 g/10 min Grade Count:124
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 20.0 - 95.020.0 - 95.0Average value: 56.4 Grade Count:57
Hardness, Rockwell R 61.0 - 11761.0 - 117Average value: 78.6 Grade Count:8
Tensile Strength, Ultimate 32.0 - 82.0 MPa4640 - 11900 psiAverage value: 50.0 MPa Grade Count:107
 45.6 - 47.8 MPa
@Temperature 18.0 - 18.0 °C		6610 - 6930 psi
@Temperature 64.4 - 64.4 °F		Average value: 46.5 MPa Grade Count:6
 45.6 - 47.8 MPa
@Time 86400 - 86400 sec		6610 - 6930 psi
@Time 24.0 - 24.0 hour		Average value: 46.5 MPa Grade Count:6
Tensile Strength, Yield 28.0 - 60.0 MPa4060 - 8700 psiAverage value: 42.2 MPa Grade Count:17
Elongation at Break 1.90 - 90.0 %1.90 - 90.0 %Average value: 30.0 % Grade Count:118
Elongation at Yield 1.90 - 40.0 %1.90 - 40.0 %Average value: 5.76 % Grade Count:38
Modulus of Elasticity 1.38 - 3.52 GPa200 - 510 ksiAverage value: 2.13 GPa Grade Count:92
Flexural Yield Strength 41.2 - 105 MPa5970 - 15200 psiAverage value: 70.0 MPa Grade Count:110
Flexural Modulus 1.36 - 3.38 GPa198 - 490 ksiAverage value: 2.11 GPa Grade Count:71
Izod Impact, Notched 0.200 - 2.45 J/cm0.375 - 4.59 ft-lb/inAverage value: 0.585 J/cm Grade Count:94
 0.240255 - 0.37373 J/cm
@Temperature 0.000 - 0.000 °C		0.450096 - 0.70015 ft-lb/in
@Temperature 32.0 - 32.0 °F		Average value: 0.330 J/cm Grade Count:6
 0.260 - 0.590 J/cm
@Temperature 0.000 - 0.000 °C		0.487 - 1.11 ft-lb/in
@Temperature 32.0 - 32.0 °F		Average value: 0.330 J/cm Grade Count:2
 0.260 - 0.590 J/cm
@Thickness 6.35 - 6.35 mm		0.487 - 1.11 ft-lb/in
@Thickness 0.250 - 0.250 in		Average value: 0.330 J/cm Grade Count:2
 0.210 - 0.64068 J/cm
@Diameter 6.35 - 6.35 mm		0.393 - 1.2003 ft-lb/in
@Diameter 0.250 - 0.250 in		Average value: 0.330 J/cm Grade Count:10
 0.210 - 0.64068 J/cm
@Temperature 0.000 - 0.000 °C		0.393 - 1.2003 ft-lb/in
@Temperature 32.0 - 32.0 °F		Average value: 0.330 J/cm Grade Count:10
Izod Impact, Unnotched 1.60 J/cm - NB3.00 ft-lb/in - NBAverage value: 3.92 J/cm Grade Count:7
Izod Impact, Notched (ISO) 2.10 - 8.00 kJ/m²0.999 - 3.81 ft-lb/in²Average value: 4.43 kJ/m² Grade Count:19
Izod Impact, Unnotched (ISO) 1.50 - 41.7 kJ/m²0.714 - 19.8 ft-lb/in²Average value: 21.8 kJ/m² Grade Count:9
 14.6 - 29.0 kJ/m²
@Temperature 0.000 - 0.000 °C		6.95 - 13.8 ft-lb/in²
@Temperature 32.0 - 32.0 °F		Average value: 24.1 kJ/m² Grade Count:4
 27.6 - 28.3 kJ/m²
@Temperature 0.000 - 0.000 °C		13.1 - 13.5 ft-lb/in²
@Temperature 32.0 - 32.0 °F		Average value: 24.1 kJ/m² Grade Count:6
 27.6 - 28.3 kJ/m²
@Time 86400 - 86400 sec		13.1 - 13.5 ft-lb/in²
@Time 24.0 - 24.0 hour		Average value: 24.1 kJ/m² Grade Count:6
Charpy Impact Unnotched 2.10 - 8.00 J/cm²9.99 - 38.1 ft-lb/in²Average value: 5.82 J/cm² Grade Count:18
Charpy Impact, Notched 0.210 - 5.40 J/cm²0.999 - 25.7 ft-lb/in²Average value: 1.36 J/cm² Grade Count:26
Gardner Impact 1.58 - 11.0 J1.17 - 8.11 ft-lbAverage value: 4.61 J Grade Count:47
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity 1.00e+14 - 1.00e+15 ohm-cm1.00e+14 - 1.00e+15 ohm-cmAverage value: 7.00e+14 ohm-cm Grade Count:15
Surface Resistance 1.00e+14 ohm1.00e+14 ohmAverage value: 1.00e+14 ohm Grade Count:7
Dielectric Constant 2.90 - 3.902.90 - 3.90Average value: 3.30 Grade Count:15
Dielectric Strength 15.0 - 60.0 kV/mm381 - 1520 kV/inAverage value: 30.0 kV/mm Grade Count:15
Dissipation Factor 0.0300 - 0.05000.0300 - 0.0500Average value: 0.0386 Grade Count:15
Comparative Tracking Index 600 V600 VAverage value: 600 V Grade Count:7
 
Thermal PropertiesMetricEnglishComments
CTE, linear 60.0 - 123 µm/m-°C33.3 - 68.3 µin/in-°FAverage value: 90.1 µm/m-°C Grade Count:88
 72.0 - 93.6 µm/m-°C
@Temperature 0.000 - 156 °C		40.0 - 52.0 µin/in-°F
@Temperature 32.0 - 312 °F		Average value: 78.6 µm/m-°C Grade Count:6
Specific Heat Capacity 1.90 - 2.30 J/g-°C
@Temperature 100 - 175 °C		0.454 - 0.550 BTU/lb-°F
@Temperature 212 - 347 °F		Average value: 2.10 J/g-°C Grade Count:1
Thermal Conductivity 0.202 - 0.220 W/m-K1.40 - 1.53 BTU-in/hr-ft²-°FAverage value: 0.210 W/m-K Grade Count:5
Maximum Service Temperature, Air 50.0 - 90.0 °C122 - 194 °FAverage value: 72.9 °C Grade Count:14
Deflection Temperature at 0.46 MPa (66 psi) 78.0 - 98.0 °C172 - 208 °FAverage value: 87.8 °C Grade Count:12
Deflection Temperature at 1.8 MPa (264 psi) 73.0 - 111 °C163 - 232 °FAverage value: 84.4 °C Grade Count:114
Vicat Softening Point 82.0 - 115 °C180 - 239 °FAverage value: 100 °C Grade Count:132
Annealing Point 60.0 - 70.0 °C140 - 158 °FAverage value: 65.0 °C Grade Count:8
Heat Distortion Temperature 80.0 - 97.0 °C176 - 207 °FAverage value: 90.3 °C Grade Count:8
Flammability, UL94 HBHBGrade Count:61
Oxygen Index 18.0 - 19.0 %18.0 - 19.0 %Average value: 18.2 % Grade Count:6
Glow Wire Test 650 °C1200 °FAverage value: 650 °C Grade Count:19
 
Optical PropertiesMetricEnglishComments
Refractive Index 1.49 - 1.571.49 - 1.57Average value: 1.50 Grade Count:51
Haze 0.500 - 98.0 %0.500 - 98.0 %Average value: 5.06 % Grade Count:93
Yellow Index -1.50 - 5.50 %-1.50 - 5.50 %Average value: 0.879 % Grade Count:19
Transmission, Visible 0.000 - 92.0 %0.000 - 92.0 %Average value: 86.3 % Grade Count:116
 
Processing PropertiesMetricEnglishComments
Processing Temperature 210 - 250 °C410 - 482 °FAverage value: 230 °C Grade Count:8
Melt Temperature 179 - 260 °C354 - 500 °FAverage value: 229 °C Grade Count:41
Mold Temperature 27.0 - 107 °C80.6 - 225 °FAverage value: 61.1 °C Grade Count:39
Drying Temperature 60.0 - 105 °C140 - 221 °FAverage value: 80.0 °C Grade Count:33
Dry Time 2.00 - 6.00 hour2.00 - 6.00 hourAverage value: 3.75 hour Grade Count:32
Injection Pressure 49.0 - 108 MPa7110 - 15700 psiAverage value: 79.4 MPa Grade Count:9
Back Pressure 0.689 - 1.38 MPa100 - 200 psiAverage value: 0.739 MPa Grade Count:7

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-29834.html

免责声明: 本文 Overview of materials for Acrylic, Impact Modified, Molded 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4