- 熔体流动速率 [g/10min]: 3.1
- 缺口冲击强度: 0.534
- 弯曲模量 [MPa]: 1.79
- 透光率 [%]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Bulk Density | 0.710 g/cc | 0.0257 lb/in³ | ASTM D1895 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D951 |
| Melt Flow | 3.1 g/10 min @Load 3.80 kg, Temperature 230 °C | 3.1 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 44 | 44 | ASTM D785 |
| Tensile Strength at Break | 44.1 MPa | 6400 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 1.72 GPa | 250 ksi | ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 1.79 GPa | 260 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Diameter 6.35 mm | 1.00 ft-lb/in @Diameter 0.250 in | BAR; ASTM D256 |
| 0.267 J/cm @Diameter 6.35 mm, Temperature 0.000 °C | 0.500 ft-lb/in @Diameter 0.250 in, Temperature 32.0 °F | BAR; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 µm/m-°C @Temperature 0.000 - 100 °C | 50.0 µin/in-°F @Temperature 32.0 - 212 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.35 mm | 185 °F @Thickness 0.250 in | Annealed; ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | 96 % | 96 % | ASTM D1003 |
| Yellow Index | 5.5 % | 5.5 % | ASTM E313 |
| Transmission, Visible | 85 % | 85 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 232 - 249 °C | 450 - 480 °F | Cylinder Temp |
| Melt Temperature | 232 - 249 °C | 450 - 480 °F | |
| Mold Temperature | 43.3 - 82.2 °C | 110 - 180 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |