- 熔体流动速率 [g/10min]: 2.6
- 缺口冲击强度: 1.07
- 弯曲模量 [MPa]: 2.41
- 透光率 [%]: 82.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D951 |
Melt Flow | 2.6 g/10 min @Load 5.00 kg, Temperature 230 °C | 2.6 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Hardness, Rockwell M | 45 | 45 | ASTM D785 |
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Elongation at Break | 28 % | 28 % | ASTM D638 |
Elongation at Yield | 3.6 % | 3.6 % | ASTM D638 |
Tensile Modulus | 2.55 GPa | 370 ksi | ASTM D638 |
Flexural Strength | 75.8 MPa | 11000 psi | ASTM D790 |
Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
Izod Impact, Notched | 1.07 J/cm @Diameter 6.35 mm | 2.00 ft-lb/in @Diameter 0.250 in | BAR; ASTM D256 |
0.854 J/cm @Diameter 6.35 mm, Temperature 0.000 °C | 1.60 ft-lb/in @Diameter 0.250 in, Temperature 32.0 °F | BAR; ASTM D256 | |
Thermal Properties | Metric | English | Comments |
CTE, linear | 90.0 µm/m-°C @Temperature 0.000 - 100 °C | 50.0 µin/in-°F @Temperature 32.0 - 212 °F | ASTM D696 |
Deflection Temperature at 1.8 MPa (264 psi) | 85.6 °C @Thickness 6.35 mm | 186 °F @Thickness 0.250 in | Annealed; ASTM D648 |
Vicat Softening Point | 103 °C | 217 °F | ASTM D1525 |
Optical Properties | Metric | English | Comments |
Refractive Index | 1.51 | 1.51 | ASTM D542 |
Haze | 4.0 % | 4.0 % | ASTM D1003 |
Yellow Index | -7.50 % | -7.50 % | ASTM E313 |
Transmission, Visible | 82 % | 82 % | ASTM D1003 |
Processing Properties | Metric | English | Comments |
Middle Barrel Temperature | 204 - 246 °C | 400 - 475 °F | Cylinder Temp |
Melt Temperature | 204 - 246 °C | 400 - 475 °F | |
Mold Temperature | 48.9 - 76.7 °C | 120 - 170 °F | |
Drying Temperature | 82.2 °C | 180 °F | |
Dry Time | 3 - 4 hour | 3 - 4 hour |