- 熔体流动速率 [g/10min]: 10.0
- 缺口冲击强度: 1.01
- 弯曲模量 [MPa]: 2.14
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D951 |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 230 °C | 10 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 27 | 27 | ASTM D785 |
| Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
| Elongation at Break | 9.5 % | 9.5 % | ASTM D638 |
| Elongation at Yield | 3.6 % | 3.6 % | ASTM D638 |
| Tensile Modulus | 2.55 GPa | 370 ksi | ASTM D638 |
| Flexural Strength | 64.8 MPa | 9400 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm @Diameter 6.35 mm | 1.90 ft-lb/in @Diameter 0.250 in | BAR; ASTM D256 |
| 0.587 J/cm @Diameter 6.35 mm, Temperature 0.000 °C | 1.10 ft-lb/in @Diameter 0.250 in, Temperature 32.0 °F | BAR; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 92.5 µm/m-°C @Temperature 0.000 - 100 °C | 51.4 µin/in-°F @Temperature 32.0 - 212 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.6 °C @Thickness 6.35 mm | 186 °F @Thickness 0.250 in | Annealed; ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.51 | 1.51 | ASTM D542 |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Yellow Index | -0.300 % | -0.300 % | ASTM E313 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 182 - 238 °C | 360 - 460 °F | Cylinder Temp |
| Melt Temperature | 193 - 238 °C | 380 - 460 °F | |
| Mold Temperature | 48.9 - 82.2 °C | 120 - 180 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |