- 熔体流动速率 [g/10min]: 3.5
- 弯曲模量 [MPa]: 3.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0070 cm/cm | 0.0060 - 0.0070 in/in | ISO 294 |
| Melt Flow | 3.5 g/10 min @Load 3.80 kg, Temperature 230 °C | 3.5 g/10 min @Load 8.38 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength at Break | 74.001 MPa | 10733 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 3.24 GPa | 470 ksi | ISO 527 |
| Flexural Strength | 95.403 MPa | 13837 psi | ISO 178 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 |
| Izod Impact, Unnotched (ISO) | 2.00 kJ/m² @Diameter 4.00 mm | 0.952 ft-lb/in² @Diameter 0.157 in | bar; ISO 180 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 75.6 µm/m-°C @Temperature 0.000 - 100 °C | 42.0 µin/in-°F @Temperature 32.0 - 212 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | annealed; ISO 75 |
| Vicat Softening Point | 106 °C | 223 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 0.0 % | 0.0 % | Opaque; ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 210 - 249 °C | 410 - 480 °F | Cylinder Temp |
| Melt Temperature | 238 - 249 °C | 460 - 480 °F | |
| Mold Temperature | 37.8 - 79.4 °C | 100 - 175 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 3 hour | 2 - 3 hour | |