- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.17
- 缺口冲击强度: 0.35
- 断裂伸长率 [%]: 79.0
- 弯曲强度 [MPa]: 52.0
- 弯曲模量 [MPa]: 2.30
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D551 |
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C | 3.0 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 64 | 64 | ASTM D785 |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 23 % | 23 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ASTM D638 |
| Flexural Yield Strength | 79.0 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| Izod Impact, Notched | 0.350 J/cm @Diameter 6.35 mm | 0.656 ft-lb/in @Diameter 0.250 in | bar; ASTM D256 |
| 0.210 J/cm @Diameter 6.35 mm, Temperature 0.000 °C | 0.393 ft-lb/in @Diameter 0.250 in, Temperature 32.0 °F | bar; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 72.0 µm/m-°C @Temperature 0.000 - 100 °C | 40.0 µin/in-°F @Temperature 32.0 - 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Annealed; ASTM D648 |
| Vicat Softening Point | 109 °C | 228 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | <= 3.0 % | <= 3.0 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 232 - 248 °C | 450 - 478 °F | |