- 熔体流动速率 [g/10min]: 11.0
- 缺口冲击强度: 0.267
- 弯曲模量 [MPa]: 1.72
- 热变形温度 [℃]: 76.9
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.01 g/cc | 1.01 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 200 °C | 11 g/10 min @Load 11.0 lb, Temperature 392 °F | Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 - 70 | 60 - 70 | ASTM D2240 |
| Tensile Strength at Break | 22.8 MPa | 3300 psi | chs 2 in/min; ASTM D638 |
| Flexural Strength | 37.2 MPa | 5400 psi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.9 °C | 170 °F | 0.125 in bar; ASTM D648 |
| Vicat Softening Point | 90.7 °C | 195 °F | 0.125 inch bar, 1 Kg; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |