- 熔体流动速率 [g/10min]: 7.4
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 45.5
- 弯曲模量 [MPa]: 2.07
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Flow | 7.4 g/10 min @Load 5.00 kg, Temperature 200 °C | 7.4 g/10 min @Load 11.0 lb, Temperature 392 °F | Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 45.5 MPa | 6600 psi | 2 in per min; ASTM D638 |
| Elongation at Break | 10 % | 10 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.07 GPa | 300 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.8 °C | 181 °F | 0.125 inch bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | 0.125 inch bar, 1 Kg; ASTM D1525 |