- 熔体流动速率 [g/10min]: 0.6
- 缺口冲击强度: 0.235
- 弯曲模量 [MPa]: 2.81
- 热变形温度 [℃]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 0.60 g/10 min @Load 5.00 kg, Temperature 200 °C | 0.60 g/10 min @Load 11.0 lb, Temperature 392 °F | Procedure A Condition G; ASTM D1238 |
| 2.6 g/10 min @Load 3.80 kg, Temperature 230 °C | 2.6 g/10 min @Load 8.38 lb, Temperature 446 °F | Procedure A Condition I; ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 57.6 MPa | 8350 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 3.19 % | 3.19 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.81 GPa | 408 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 0.235 J/cm | 0.440 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Vicat Softening Point | 103 °C | 217 °F | ASTM D1525 |