- 密度 [g/cm3]: 1.35
- 缺口冲击强度: 6.0
- 断裂伸长率 [%]: 69.0
- 弯曲强度 [MPa]: 41.0
- 硬度: 108.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | |
| Modulus of Elasticity | 2.517 GPa | 365.1 ksi | |
| Flexural Yield Strength | 69.0 MPa | 10000 psi | ASTM D790 |
| Izod Impact, Notched | 6.00 - 9.00 J/cm @Temperature 23.0 °C | 11.2 - 16.9 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 162 - 200 °C | 324 - 392 °F | Forming Temperature |