- 密度 [g/cm3]: 1.35
- 缺口冲击强度: 5.34
- 断裂伸长率 [%]: 63.0
- 弯曲强度 [MPa]: 42.0
- 硬度: 94.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength, Ultimate | 42.0 MPa | 6090 psi | ASTM D638 |
| Elongation at Break | 80 % | 80 % | |
| Modulus of Elasticity | 2.206 GPa | 320.0 ksi | |
| Flexural Yield Strength | 63.0 MPa | 9140 psi | ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm @Temperature 23.0 °C | 10.0 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | annealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | Independent Test Lab |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 163 - 200 °C | 325 - 392 °F | Forming Temperature |