- 密度 [g/cm3]: 1.17
- 缺口冲击强度: 5.0
- 弯曲强度 [MPa]: 68.0
- 弯曲模量 [MPa]: 2.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 65 | 65 | ISO 2039-2 |
| Tensile Strength, Ultimate | 68.0 MPa | 9860 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 18 % | 18 % | 5 mm/min; ISO 527 |
| Flexural Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | >= 105 °C | >= 221 °F | ISO 306A |
| Flammability, UL94 | HB | HB | |