- 吸水率 [%]: 0.4
- 缺口冲击强度: 0.589
- 弯曲模量 [MPa]: 1.373
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Index of Compound | 0.90 g/10 min @Load 3.80 kg, Temperature 230 °C | 0.90 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 44 | 44 | ASTM D785 |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Elongation at Break | 90 % | 90 % | ASTM D638 |
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Flexural Modulus | 1.373 GPa | 199.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.589 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 60 Hz | 3.5 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | 4kV/s; ASTM D149 |
| Dissipation Factor | 0.040 @Frequency 60 Hz | 0.040 @Frequency 60 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 µm/m-°C @Temperature 20.0 °C | 33.3 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ASTM D648 |
| Vicat Softening Point | 92.0 °C | 198 °F | 1 kg; ASTM D1525 |
| Annealing Point | 60.0 - 70.0 °C | 140 - 158 °F | 3-5 hours |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | 1.5 % @Thickness 3.20 mm | 1.5 % @Thickness 0.126 in | ASTM D1003 |
| Transmission, Visible | 90 % @Thickness 3.20 mm | 90 % @Thickness 0.126 in | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 210 - 250 °C | 410 - 482 °F | Injection molding cylinder temperature |
| Mold Temperature | 60.0 - 70.0 °C | 140 - 158 °F | |
| Drying Temperature | 60.0 - 70.0 °C | 140 - 158 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Injection Pressure | 49.0 - 108 MPa | 7110 - 15700 psi | |