- 熔体流动速率 [g/10min]: 13.0
- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 0.3
- 缺口冲击强度: 2.1
- 弯曲模量 [MPa]: 2.40
- 透光率 [%]: 91.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 13 g/10 min | 13 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 78 | 78 | ISO 2039-2 |
| Tensile Strength | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 6.0 % | 6.0 % | ISO 527 |
| Flexural Strength | 85.0 MPa | 12300 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.10 kJ/m² | 0.999 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 2.10 J/cm² | 9.99 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.210 J/cm² | 0.999 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ASTM E831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ISO 75A |
| Vicat Softening Point | 91.0 °C | 196 °F | ISO 306B |
| 97.0 °C | 207 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Transmission, Visible | 91.5 % | 91.5 % | ASTM D1003 |