- 熔体流动速率 [g/10min]: 5.6
- 密度 [g/cm3]: 1.05
- 吸水率 [%]: 0.1
- 缺口冲击强度: 1.6
- 拉伸强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 2.07
- 硬度: 61.0
- 透光率 [%]: 87.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 5.6 g/10 min @Load 5.00 kg, Temperature 200 °C | 5.6 g/10 min @Load 11.0 lb, Temperature 392 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 61 | 61 | ASTM D785 |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 0.2 in/min; ASTM D638 |
| Elongation at Break | 53 % | 53 % | 0.2 in/min; ASTM D638 |
| Modulus of Elasticity | 2.34 GPa | 339 ksi | 0.2 in/min; ASTM D638 |
| Flexural Strength | 49.0 MPa | 7110 psi | 0.5 in/min; ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | 0.5 in/min; ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Annealed; ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.56 | 1.56 | ASTM D542 |
| Haze | 3.1 % | 3.1 % | ASTM D1003 |
| Transmission, Visible | 87.5 % | 87.5 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | <= 238 °C | <= 460 °F | |
| Rear Barrel Temperature | 179 - 213 °C | 354 - 415 °F | |
| Middle Barrel Temperature | 185 - 218 °C | 365 - 424 °F | |
| Front Barrel Temperature | 191 - 224 °C | 376 - 435 °F | |
| Melt Temperature | 204 - 238 °C | 399 - 460 °F | |
| Mold Temperature | 27.0 - 54.0 °C | 80.6 - 129 °F | |
| Drying Temperature | 68.0 °C | 154 °F | |
| Dry Time | 2 hour | 2 hour | |