- 熔体流动速率 [g/10min]: 16.0
- 缺口冲击强度: 2.45
- 拉伸强度 [MPa]: 54.9
- 弯曲模量 [MPa]: 2.31
- 硬度: 117.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 | ||
| Melt Flow | 16 g/10 min @Load 10.0 kg, Temperature 220 °C | 16 g/10 min @Load 22.0 lb, Temperature 428 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 117 | 117 | ASTM D785 | ||
| Tensile Strength, Yield | 54.9 MPa | 7970 psi | 5 mm/min; ASTM D638 | ||
| Flexural Strength | 79.4 MPa | 11500 psi | 2.8 mm/min; ASTM D790 | ||
| Flexural Modulus | 2.31 GPa | 336 ksi | 2.8 mm/min; ASTM D790 | ||
| Izod Impact, Notched | 2.45 J/cm @Thickness 6.35 mm | 4.59 ft-lb/in @Thickness 0.250 in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C @Thickness 6.40 mm | 171 °F @Thickness 0.252 in | ASTM D648 | ||
| Vicat Softening Point | 92.0 °C | 198 °F | B/50; ISO R306 | ||
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm | HB @Thickness 0.0591 - 0.118 in | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 0.50 % @Thickness 2.50 mm | 0.50 % @Thickness 0.0984 in | ASTM D1003 | ||
| Descriptive Properties | |||||
| Pencil Hardness | 3H | 500g, JIS K 5401 | |||