- 熔体流动速率 [g/10min]: 8.0
- 缺口冲击强度: 0.235
- 断裂伸长率 [%]: 95.1
- 弯曲模量 [MPa]: 2.40
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 73.5 MPa | 10700 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Flexural Yield Strength | 95.1 MPa | 13800 psi | ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Izod Impact, Notched | 0.235 J/cm @Thickness 3.17 mm | 0.441 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |