- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.95
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 16.0
- 断裂伸长率 [%]: 20.0
- 弯曲强度 [MPa]: 10.0
- 弯曲模量 [MPa]: 1.07
- 硬度: 40.0
- 热变形温度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 - 1.14 g/cc | 0.0343 - 0.0414 lb/in³ | Average value: 1.03 g/cc Grade Count:43 |
| Filler Content | 15.0 - 20.0 % | 15.0 - 20.0 % | Average value: 17.8 % Grade Count:9 |
| Linear Mold Shrinkage | 0.000900 - 0.0120 cm/cm | 0.000900 - 0.0120 in/in | Average value: 0.00745 cm/cm Grade Count:41 |
| Melt Flow | 3.00 - 56.0 g/10 min | 3.00 - 56.0 g/10 min | Average value: 16.6 g/10 min Grade Count:41 |
| Ash | 20.0 % | 20.0 % | Average value: 20.0 % Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 40.0 - 97.0 | 40.0 - 97.0 | Average value: 70.5 Grade Count:12 |
| Hardness, Shore D | 68.0 - 76.0 | 68.0 - 76.0 | Average value: 74.3 Grade Count:8 |
| Ball Indentation Hardness | 23.0 - 63.0 MPa | 3340 - 9140 psi | Average value: 39.4 MPa Grade Count:14 |
| Tensile Strength, Ultimate | 10.0 - 35.2 MPa | 1450 - 5110 psi | Average value: 26.2 MPa Grade Count:22 |
| Tensile Strength, Yield | 16.0 - 38.6 MPa | 2320 - 5600 psi | Average value: 23.6 MPa Grade Count:32 |
| Elongation at Break | 4.90 - 300 % | 4.90 - 300 % | Average value: 55.0 % Grade Count:26 |
| Elongation at Yield | 2.60 - 8.00 % | 2.60 - 8.00 % | Average value: 5.17 % Grade Count:27 |
| Modulus of Elasticity | 1.00 - 3.10 GPa | 145 - 450 ksi | Average value: 1.86 GPa Grade Count:29 |
| Flexural Yield Strength | 20.0 - 51.0 MPa | 2900 - 7400 psi | Average value: 32.2 MPa Grade Count:28 |
| Flexural Modulus | 1.07 - 3.59 GPa | 155 - 520 ksi | Average value: 2.15 GPa Grade Count:43 |
| Izod Impact, Notched | 0.267 - 1.98 J/cm | 0.500 - 3.70 ft-lb/in | Average value: 0.530 J/cm Grade Count:23 |
| Izod Impact, Unnotched | 2.70 - 5.23 J/cm | 5.06 - 9.80 ft-lb/in | Average value: 3.71 J/cm Grade Count:3 |
| Izod Impact, Notched (ISO) | 6.40 - 50.0 kJ/m² | 3.05 - 23.8 ft-lb/in² | Average value: 33.0 kJ/m² Grade Count:13 |
| 2.60 - 15.0 kJ/m² @Temperature -20.0 - -20.0 °C | 1.24 - 7.14 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 5.34 kJ/m² Grade Count:13 | |
| Izod Impact, Unnotched (ISO) | 27.0 - 42.0 kJ/m² @Temperature -20.0 - -20.0 °C | 12.8 - 20.0 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 34.5 kJ/m² Grade Count:2 |
| Charpy Impact Unnotched | 6.30 - 1000 J/cm² | 30.0 - 4760 ft-lb/in² | Average value: 12.6 J/cm² Grade Count:18 |
| 2.90 - 999.9 J/cm² @Temperature -20.0 - -20.0 °C | 13.8 - 4759 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 7.04 J/cm² Grade Count:18 | |
| Charpy Impact, Notched | 0.650 - 6.00 J/cm² | 3.09 - 28.6 ft-lb/in² | Average value: 3.20 J/cm² Grade Count:20 |
| 0.200 - 0.700 J/cm² @Temperature -30.0 - -20.0 °C | 0.952 - 3.33 ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 0.445 J/cm² Grade Count:20 | |
| Gardner Impact | 0.339 - 1.81 J | 0.250 - 1.33 ft-lb | Average value: 0.698 J Grade Count:12 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 - 80.0 µm/m-°C | 16.7 - 44.4 µin/in-°F | Average value: 53.1 µm/m-°C Grade Count:11 |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 - 132 °C | 176 - 270 °F | Average value: 108 °C Grade Count:40 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 - 79.0 °C | 117 - 174 °F | Average value: 60.0 °C Grade Count:41 |
| Vicat Softening Point | 36.0 - 150 °C | 96.8 - 302 °F | Average value: 89.8 °C Grade Count:20 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | Average value: 240 °C Grade Count:20 |
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Average value: 60.0 °C Grade Count:19 |
| Nozzle Temperature | 210 - 227 °C | 410 - 440 °F | Average value: 219 °C Grade Count:7 |
| Melt Temperature | 193 - 238 °C | 380 - 460 °F | Average value: 216 °C Grade Count:7 |
| Mold Temperature | 26.7 - 50.0 °C | 80.0 - 122 °F | Average value: 39.4 °C Grade Count:27 |
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | Average value: 150 mm/sec Grade Count:20 |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | Average value: 73.9 °C Grade Count:7 |
| Dry Time | 1.00 - 2.00 hour | 1.00 - 2.00 hour | Average value: 1.50 hour Grade Count:7 |
| Moisture Content | 0.0500 % | 0.0500 % | Average value: 0.0500 % Grade Count:7 |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | Average value: 6.55 MPa Grade Count:7 |
| Hold Pressure | 2.07 - 60.0 MPa | 300 - 8700 psi | Average value: 27.2 MPa Grade Count:27 |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi | Average value: 0.689 MPa Grade Count:7 |