- 熔体流动速率 [g/10min]: 0.4
- 密度 [g/cm3]: 1.01
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 36.0
- 断裂伸长率 [%]: 32.0
- 弯曲强度 [MPa]: 6.89
- 弯曲模量 [MPa]: 1.60
- 硬度: 81.0
- 热变形温度 [℃]: 99.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 - 1.51 g/cc | 0.0365 - 0.0546 lb/in³ | Average value: 1.14 g/cc Grade Count:270 |
| Filler Content | 25.0 - 35.0 % | 25.0 - 35.0 % | Average value: 29.6 % Grade Count:93 |
| Water Absorption | 0.0100 - 0.0500 % | 0.0100 - 0.0500 % | Average value: 0.0269 % Grade Count:44 |
| Additive Loading | 25.0 - 30.0 % | 25.0 - 30.0 % | Average value: 29.4 % Grade Count:8 |
| Maximum Moisture Content | 0.0100 | 0.0100 | Average value: 0.0100 Grade Count:3 |
| Linear Mold Shrinkage | 0.000600 - 0.0200 cm/cm | 0.000600 - 0.0200 in/in | Average value: 0.00412 cm/cm Grade Count:206 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | Average value: 0.00467 cm/cm Grade Count:12 |
| Linear Mold Shrinkage, Transverse | 0.00230 - 0.0193 cm/cm | 0.00230 - 0.0193 in/in | Average value: 0.0101 cm/cm Grade Count:30 |
| Melt Flow | 0.400 - 25.0 g/10 min | 0.400 - 25.0 g/10 min | Average value: 6.78 g/10 min Grade Count:183 |
| Ash | 26.0 - 32.0 % | 26.0 - 32.0 % | Average value: 29.9 % Grade Count:11 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 57.0 - 107 | 57.0 - 107 | Average value: 68.5 Grade Count:11 |
| Hardness, Rockwell R | 81.0 - 115 | 81.0 - 115 | Average value: 99.2 Grade Count:44 |
| Hardness, Shore D | 47.0 - 76.0 | 47.0 - 76.0 | Average value: 71.9 Grade Count:23 |
| Ball Indentation Hardness | 110 - 132 MPa | 16000 - 19100 psi | Average value: 117 MPa Grade Count:7 |
| Tensile Strength, Ultimate | 6.89 - 130 MPa | 1000 - 18900 psi | Average value: 78.5 MPa Grade Count:168 |
| 9.00 - 140.653 MPa @Temperature -40.0 - 120 °C | 1310 - 20400.0 psi @Temperature -40.0 - 248 °F | Average value: 42.4 MPa Grade Count:13 | |
| Tensile Strength, Yield | 36.0 - 110 MPa | 5220 - 16000 psi | Average value: 76.5 MPa Grade Count:109 |
| Elongation at Break | 1.00 - 30.0 % | 1.00 - 30.0 % | Average value: 3.78 % Grade Count:175 |
| 2.00 - 5.00 % @Temperature -40.0 - 93.3 °C | 2.00 - 5.00 % @Temperature -40.0 - 200 °F | Average value: 3.07 % Grade Count:8 | |
| Elongation at Yield | 2.00 - 9.40 % | 2.00 - 9.40 % | Average value: 3.63 % Grade Count:60 |
| Modulus of Elasticity | 2.25 - 9.65 GPa | 326 - 1400 ksi | Average value: 6.20 GPa Grade Count:121 |
| 3.50 - 8.68739 GPa @Temperature -40.0 - 93.3 °C | 508 - 1260.02 ksi @Temperature -40.0 - 200 °F | Average value: 4.69 GPa Grade Count:8 | |
| Flexural Yield Strength | 32.0 - 170 MPa | 4640 - 24700 psi | Average value: 111 MPa Grade Count:193 |
| 82.0 - 234.422 MPa @Temperature -40.0 - 121 °C | 11900 - 34000.1 psi @Temperature -40.0 - 250 °F | Average value: 117 MPa Grade Count:4 | |
| Flexural Modulus | 1.60 - 9.90 GPa | 232 - 1440 ksi | Average value: 5.20 GPa Grade Count:258 |
| 1.60 - 8.34266 GPa @Temperature -40.0 - 121 °C | 232 - 1210.02 ksi @Temperature -40.0 - 250 °F | Average value: 4.15 GPa Grade Count:9 | |
| Compressive Yield Strength | 57.9 - 82.7 MPa | 8400 - 12000 psi | Average value: 71.7 MPa Grade Count:7 |
| Izod Impact, Notched | 0.320 - 3.26 J/cm | 0.599 - 6.10 ft-lb/in | Average value: 1.09 J/cm Grade Count:178 |
| 0.300 - 4.35 J/cm @Temperature -40.0 - 121 °C | 0.562 - 8.15 ft-lb/in @Temperature -40.0 - 250 °F | Average value: 1.08 J/cm Grade Count:15 | |
| 0.5339 - 0.5339 J/cm @Temperature -28.9 - -28.9 °C | 1.000 - 1.000 ft-lb/in @Temperature -20.0 - -20.0 °F | Average value: 1.08 J/cm Grade Count:1 | |
| 0.5339 - 0.5339 J/cm @Thickness 3.17 - 3.17 mm | 1.000 - 1.000 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 1.08 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 0.650 - 8.54 J/cm | 1.22 - 16.0 ft-lb/in | Average value: 4.98 J/cm Grade Count:76 |
| 0.450 - 1.10 J/cm @Temperature 0.000 - 0.000 °C | 0.843 - 2.06 ft-lb/in @Temperature 32.0 - 32.0 °F | Average value: 0.788 J/cm Grade Count:4 | |
| Izod Impact, Notched (ISO) | 6.00 - 38.0 kJ/m² | 2.86 - 18.1 ft-lb/in² | Average value: 14.8 kJ/m² Grade Count:25 |
| 4.60 - 16.0 kJ/m² @Temperature -40.0 - -20.0 °C | 2.19 - 7.61 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 8.37 kJ/m² Grade Count:15 | |
| Izod Impact, Unnotched (ISO) | 28.0 - 55.0 kJ/m² | 13.3 - 26.2 ft-lb/in² | Average value: 45.8 kJ/m² Grade Count:6 |
| 18.0 - 68.0 kJ/m² @Temperature -45.0 - -30.0 °C | 8.57 - 32.4 ft-lb/in² @Temperature -49.0 - -22.0 °F | Average value: 42.8 kJ/m² Grade Count:6 | |
| Charpy Impact Unnotched | 0.600 - 1000 J/cm² | 2.86 - 4760 ft-lb/in² | Average value: 4.78 J/cm² Grade Count:57 |
| 0.400 - 8.00 J/cm² @Temperature -40.0 - -20.0 °C | 1.90 - 38.1 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 3.99 J/cm² Grade Count:44 | |
| Charpy Impact, Notched | 0.280 - 3.10 J/cm² | 1.33 - 14.8 ft-lb/in² | Average value: 1.30 J/cm² Grade Count:77 |
| 0.100 - 2.80 J/cm² @Temperature -40.0 - -20.0 °C | 0.476 - 13.3 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 1.01 J/cm² Grade Count:56 | |
| Gardner Impact | 0.300 - 13.6 J | 0.221 - 10.0 ft-lb | Average value: 1.39 J Grade Count:36 |
| 2.71164 - 2.71164 J @Temperature -5.56 - -5.56 °C | 2.00000 - 2.00000 ft-lb @Temperature 22.0 - 22.0 °F | Average value: 2.71 J Grade Count:1 | |
| Puncture Energy | 21.0 - 21.0 J @Temperature -30.0 - -30.0 °C | 15.5 - 15.5 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 21.0 J Grade Count:1 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1000 - 3.00e+16 ohm-cm | 1000 - 3.00e+16 ohm-cm | Average value: 3.87e+15 ohm-cm Grade Count:28 |
| Surface Resistance | 100000 - 1.00e+15 ohm | 100000 - 1.00e+15 ohm | Average value: 3.35e+14 ohm Grade Count:5 |
| Dielectric Constant | 2.60 - 3.30 | 2.60 - 3.30 | Average value: 2.93 Grade Count:11 |
| Dielectric Strength | 17.7 - 40.0 kV/mm | 450 - 1020 kV/in | Average value: 22.4 kV/mm Grade Count:20 |
| Dissipation Factor | 0.00100 - 0.00300 | 0.00100 - 0.00300 | Average value: 0.00160 Grade Count:10 |
| Arc Resistance | 85.0 - 125 sec | 85.0 - 125 sec | Average value: 109 sec Grade Count:8 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:14 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 26.0 - 70.0 µm/m-°C | 14.4 - 38.9 µin/in-°F | Average value: 39.8 µm/m-°C Grade Count:26 |
| Thermal Conductivity | 0.270 - 0.331 W/m-K | 1.87 - 2.30 BTU-in/hr-ft²-°F | Average value: 0.319 W/m-K Grade Count:9 |
| Melting Point | 145 - 193 °C | 293 - 380 °F | Average value: 164 °C Grade Count:42 |
| Maximum Service Temperature, Air | 65.0 - 140 °C | 149 - 284 °F | Average value: 113 °C Grade Count:8 |
| Hot Ball Pressure Test | 125 °C | 257 °F | Average value: 125 °C Grade Count:4 |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 - 165 °C | 210 - 329 °F | Average value: 154 °C Grade Count:160 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 - 162 °C | 144 - 324 °F | Average value: 143 °C Grade Count:232 |
| Deflection Temperature at 8.0 MPa | 117 - 134 °C | 243 - 273 °F | Average value: 123 °C Grade Count:12 |
| Vicat Softening Point | 70.0 - 166 °C | 158 - 331 °F | Average value: 137 °C Grade Count:72 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:124 |
| Flammability Test | 0.800 - 125 | 0.800 - 125 | Average value: 43.3 Grade Count:14 |
| Oxygen Index | 20.0 - 29.0 % | 20.0 - 29.0 % | Average value: 22.1 % Grade Count:15 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 735 °C Grade Count:39 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 30.0 - 280 °C | 86.0 - 536 °F | Average value: 150 °C Grade Count:43 |
| Feed Temperature | 20.0 - 240 °C | 68.0 - 464 °F | Average value: 57.0 °C Grade Count:30 |
| Nozzle Temperature | 200 - 260 °C | 392 - 500 °F | Average value: 229 °C Grade Count:35 |
| Die Temperature | 220 - 270 °C | 428 - 518 °F | Average value: 244 °C Grade Count:18 |
| Melt Temperature | 145 - 302 °C | 293 - 576 °F | Average value: 229 °C Grade Count:141 |
| Mold Temperature | 4.00 - 100 °C | 39.2 - 212 °F | Average value: 52.2 °C Grade Count:147 |
| Injection Velocity | 13.0 - 3330 mm/sec | 0.512 - 131 in/sec | Average value: 337 mm/sec Grade Count:10 |
| Drying Temperature | 51.7 - 100 °C | 125 - 212 °F | Average value: 80.3 °C Grade Count:105 |
| Dry Time | 1.00 - 4.00 hour | 1.00 - 4.00 hour | Average value: 2.70 hour Grade Count:85 |
| Moisture Content | 0.0100 - 0.200 % | 0.0100 - 0.200 % | Average value: 0.118 % Grade Count:42 |
| Injection Pressure | 2.76 - 120 MPa | 400 - 17400 psi | Average value: 71.2 MPa Grade Count:105 |
| Hold Pressure | 2.07 - 80.0 MPa | 300 - 11600 psi | Average value: 33.2 MPa Grade Count:40 |
| Back Pressure | 0.150 - 58.8 MPa | 21.8 - 8530 psi | Average value: 3.78 MPa Grade Count:58 |
| Screw Speed | 25.0 - 150 rpm | 25.0 - 150 rpm | Average value: 40.3 rpm Grade Count:22 |
| Hot-Working Temperature | 210 - 270 °C | 410 - 518 °F | Average value: 249 °C Grade Count:14 |