- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.96
- 缺口冲击强度: 0.43
- 拉伸强度 [MPa]: 14.7
- 断裂伸长率 [%]: 15.7
- 弯曲强度 [MPa]: 14.0
- 弯曲模量 [MPa]: 1.02
- 硬度: 69.0
- 热变形温度 [℃]: 76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 - 1.34 g/cc | 0.0347 - 0.0484 lb/in³ | Average value: 1.07 g/cc Grade Count:42 |
| Maximum Moisture Content | 0.0100 | 0.0100 | Average value: 0.0100 Grade Count:26 |
| Linear Mold Shrinkage | 0.00200 - 0.0400 cm/cm | 0.00200 - 0.0400 in/in | Average value: 0.0108 cm/cm Grade Count:35 |
| Linear Mold Shrinkage, Transverse | 0.00700 - 0.0120 cm/cm | 0.00700 - 0.0120 in/in | Average value: 0.00995 cm/cm Grade Count:4 |
| Melt Flow | 3.00 - 40.0 g/10 min | 3.00 - 40.0 g/10 min | Average value: 15.9 g/10 min Grade Count:36 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 69.0 - 90.0 | 69.0 - 90.0 | Average value: 86.0 Grade Count:7 |
| Tensile Strength, Ultimate | 14.0 - 26.0 MPa | 2030 - 3770 psi | Average value: 18.9 MPa Grade Count:11 |
| Tensile Strength, Yield | 14.7 - 65.8 MPa | 2130 - 9550 psi | Average value: 25.0 MPa Grade Count:31 |
| Elongation at Break | 4.00 - 300 % | 4.00 - 300 % | Average value: 85.9 % Grade Count:39 |
| Modulus of Elasticity | 1.10 - 2.40 GPa | 160 - 348 ksi | Average value: 1.78 GPa Grade Count:4 |
| Flexural Yield Strength | 15.7 - 97.2 MPa | 2280 - 14100 psi | Average value: 35.2 MPa Grade Count:37 |
| Flexural Modulus | 1.02 - 4.55 GPa | 148 - 660 ksi | Average value: 2.03 GPa Grade Count:39 |
| Izod Impact, Notched | 0.430 - 4.90 J/cm | 0.806 - 9.19 ft-lb/in | Average value: 2.11 J/cm Grade Count:36 |
| >= 0.343233 J/cm @Temperature -30.0 - -10.0 °C | >= 0.643016 ft-lb/in @Temperature -22.0 - 14.0 °F | Average value: 0.537 J/cm Grade Count:17 | |
| >= 0.343233 J/cm @Thickness 6.40 - 6.40 mm | >= 0.643016 ft-lb/in @Thickness 0.252 - 0.252 in | Average value: 0.537 J/cm Grade Count:17 | |
| Izod Impact, Unnotched | 2.08 J/cm - NB | 3.90 ft-lb/in - NB | Average value: 5.69 J/cm Grade Count:7 |
| Charpy Impact Unnotched | 3.80 - 1000 J/cm² | 18.1 - 4760 ft-lb/in² | Average value: 4.90 J/cm² Grade Count:6 |
| 1.40 - 999.9 J/cm² @Temperature -40.0 - -20.0 °C | 6.66 - 4759 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 1.40 J/cm² Grade Count:3 | |
| Charpy Impact, Notched | 0.300 - 7.50 J/cm² | 1.43 - 35.7 ft-lb/in² | Average value: 2.89 J/cm² Grade Count:5 |
| 2.00 - 4.80 J/cm² @Temperature -20.0 - -20.0 °C | 9.52 - 22.8 ft-lb/in² @Temperature -4.00 - -4.00 °F | Average value: 3.40 J/cm² Grade Count:2 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 - 145 °C | 169 - 293 °F | Average value: 117 °C Grade Count:35 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 - 146 °C | 124 - 295 °F | Average value: 69.8 °C Grade Count:13 |
| Vicat Softening Point | 100 - 140 °C | 212 - 284 °F | Average value: 120 °C Grade Count:4 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | Average value: 220 °C Grade Count:26 |
| Melt Temperature | 190 - 250 °C | 374 - 482 °F | Average value: 212 °C Grade Count:30 |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Average value: 50.7 °C Grade Count:30 |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Average value: 75.4 °C Grade Count:28 |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Average value: 3.50 hour Grade Count:26 |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Average value: 44.1 MPa Grade Count:26 |
| Screw Speed | 30.0 - 60.0 rpm | 30.0 - 60.0 rpm | Average value: 45.0 rpm Grade Count:26 |