- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 1.2
- 缺口冲击强度: 1.07
- 拉伸强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 1.00
- 热变形温度 [℃]: 70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM D955 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Tensile Modulus | 0.800 GPa | 116 ksi | ASTM D638 |
| Flexural Strength | 27.6 MPa | 4000 psi | ASTM D790 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | |
| Flammability, UL94 | V-0 @Thickness 3.17 mm | V-0 @Thickness 0.125 in | UL File #99379(N) |