- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.2
- 缺口冲击强度: 2.14
- 拉伸强度 [MPa]: 58.0
- 弯曲模量 [MPa]: 5.699
- 硬度: 91.0
- 热变形温度 [℃]: 158.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 91 | 91 | ASTM D785 |
| Tensile Strength at Break | 57.0 MPa | 8270 psi | ASTM D638 |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 4.000 GPa | 580.1 ksi | ASTM D638 |
| Flexural Strength | 87.98 MPa | 12760 psi | ASTM D790 |
| Flexural Modulus | 5.699 GPa | 826.6 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm | 4.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | |