- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.24
- 缺口冲击强度: 0.299
- 拉伸强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 3.699
- 硬度: 83.0
- 热变形温度 [℃]: 128.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 83 | 83 | ASTM D785 |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 12 % | 12 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.499 GPa | 362.5 ksi | ASTM D638 |
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Flexural Modulus | 3.699 GPa | 536.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.299 J/cm | 0.560 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |