- 密度 [g/cm3]: 0.92
- 拉伸强度 [MPa]: 21.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1183 |
| Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C | 35 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ISO R 527 |
| Elongation at Break | 500 % | 500 % | ISO R 527 |
| Tensile Modulus | 0.680 GPa | 98.6 ksi | ISO R 527 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 160 °C | 320 °F | DSC |
| Vicat Softening Point | 121 °C | 250 °F | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 275 °C | 527 °F | |
| Adapter Temperature | 275 °C | 527 °F | |
| Die Temperature | 275 °C | 527 °F | |