- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 1.12
- 拉伸强度 [MPa]: 19.0
- 热变形温度 [℃]: 102.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | 50 mm/min |
| Elongation at Break | 26 % | 26 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min |
| Tensile Modulus | 1.92 GPa | 278 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | |
| 0.360 J/cm² @Temperature -30.0 °C | 1.71 ft-lb/in² @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 161 °C | 322 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | |
| Vicat Softening Point | 52.0 °C | 126 °F | 50°C/hr; 50N |