- 密度 [g/cm3]: 0.89
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.890 g/cc | 0.0322 lb/in³ | ISO 1183 |
| Particle Size | <= 125 µm | <= 125 µm | 0.2 |
| 100 - 300 µm | 100 - 300 µm | 0.65 | |
| 300 - 400 µm | 300 - 400 µm | 0.15 | |
| >= 400 µm | >= 400 µm | 0 | |
| Melt Index of Compound | 6.0 - 10 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 - 10 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 6.0 | 6.0 | ISO 608 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO R 527-2 |
| Elongation at Break | 500 % | 500 % | ISO R 527-2 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 134 °C | 273 °F | DSC |
| Vicat Softening Point | 120 °C @Load 0.999 kg | 248 °F @Load 2.20 lb | ISO 306 |