A. Schulman ComAlloy Voloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled, Flame Retardant

A. Schulman ComAlloy Voloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled, Flame Retardant 物性表: A. Schulman ComAlloy Voloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled, Flame Retardant物性表及特性介绍,A. Schulman ComAlloy Voloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled, Flame Retardant注塑参数详情,如需A. Schulman ComAlloy Voloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled, Flame Retardant下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.5
  • 缺口冲击强度: 0.64
  • 弯曲强度 [MPa]: 68.0
  • 弯曲模量 [MPa]: 7.40
  • 硬度: 106.0
  • 热变形温度 [℃]: 152.0
 
Physical PropertiesMetricEnglishComments
Density 1.50 g/cc0.0542 lb/in³
Linear Mold Shrinkage 0.0040 cm/cm0.0040 in/inASTM D955
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 106106ASTM D785
Tensile Strength, Ultimate 68.0 MPa9860 psiASTM D638
Elongation at Break 3.0 %3.0 %ASTM D638
Flexural Strength 96.0 MPa13900 psiASTM D790
Flexural Modulus 7.40 GPa1070 ksiASTM D790
Izod Impact, Notched 0.640 J/cm1.20 ft-lb/inASTM D256
Izod Impact, Unnotched 2.83 J/cm5.30 ft-lb/inASTM D256
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 152 °C306 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 138 °C280 °FASTM D648
 
Processing PropertiesMetricEnglishComments
Processing Temperature 229 - 246 °C444 - 475 °FApproximate middle barrel temperature range

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31104.html

免责声明: 本文 A. Schulman ComAlloy Voloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled, Flame Retardant 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4