- 熔体流动速率 [g/10min]: 12.0
- 缺口冲击强度: 0.3
- 拉伸强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 2.00
- 热变形温度 [℃]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 0.300 J/cm | 0.562 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| UL RTI, Electrical | 105 °C @Thickness 0.780 mm | 221 °F @Thickness 0.0307 in | UL 94 |
| Flammability, UL94 | V-0 @Thickness 0.780 mm | V-0 @Thickness 0.0307 in | |
| V-0 @Thickness 1.57 mm | V-0 @Thickness 0.0618 in | ||
| V-0 @Thickness 3.05 mm | V-0 @Thickness 0.120 in | ||