- 熔体流动速率 [g/10min]: 8.0
- 缺口冲击强度: 1.6
- 拉伸强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 3.40
- 硬度: 90.0
- 热变形温度 [℃]: 150.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 70.0 MPa | 10200 psi | ASTM D790 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ASTM D648 |