- 熔体流动速率 [g/10min]: 10.0
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 36.0
- 弯曲模量 [MPa]: 2.275
- 热变形温度 [℃]: 125.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Modulus | 2.275 GPa | 330.0 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | ASTM D648 |
| UL RTI, Electrical | 65.0 °C @Thickness 0.780 mm | 149 °F @Thickness 0.0307 in | UL 746 |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.780 mm | 149 °F @Thickness 0.0307 in | UL 746 |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.780 mm | 149 °F @Thickness 0.0307 in | UL 746 |
| Flammability, UL94 | HB @Thickness 0.780 mm | HB @Thickness 0.0307 in | |