- 熔体流动速率 [g/10min]: 2.0
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 34.0
- 弯曲模量 [MPa]: 3.31
- 热变形温度 [℃]: 130.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
| Flexural Modulus | 3.31 GPa | 480 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| UL RTI, Electrical | 120 °C @Thickness 0.780 mm | 248 °F @Thickness 0.0307 in | UL 746 |
| 120 °C @Thickness 1.57 mm | 248 °F @Thickness 0.0618 in | UL 746 | |
| 120 °C @Thickness 3.17 mm | 248 °F @Thickness 0.125 in | UL 746 | |
| UL RTI, Mechanical with Impact | 115 °C @Thickness 0.780 mm | 239 °F @Thickness 0.0307 in | UL 746 |
| 115 °C @Thickness 1.57 mm | 239 °F @Thickness 0.0618 in | UL 746 | |
| 115 °C @Thickness 3.17 mm | 239 °F @Thickness 0.125 in | UL 746 | |
| UL RTI, Mechanical without Impact | 115 °C @Thickness 0.780 - 1.57 mm | 239 °F @Thickness 0.0307 - 0.0618 in | UL 746 |
| 120 °C @Thickness 3.17 mm | 248 °F @Thickness 0.125 in | UL 746 | |
| Flammability, UL94 | HB @Thickness 0.780 mm | HB @Thickness 0.0307 in | |
| HB @Thickness 1.57 mm | HB @Thickness 0.0618 in | ||
| HB @Thickness 3.17 mm | HB @Thickness 0.125 in | ||