- 熔体流动速率 [g/10min]: 20.0
- 缺口冲击强度: 0.27
- 拉伸强度 [MPa]: 29.7
- 弯曲模量 [MPa]: 3.585
- 硬度: 97.0
- 热变形温度 [℃]: 132.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Melt Flow | 20 - 30 g/10 min @Temperature 230 °C | 20 - 30 g/10 min @Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 97 | 97 | ASTM D785 |
| Tensile Strength, Yield | 29.7 MPa | 4310 psi | ASTM D638 |
| Flexural Modulus | 3.585 GPa | 520.0 ksi | ASTM D790 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.68 J/cm | 5.02 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |