- 熔体流动速率 [g/10min]: 10.0
- 缺口冲击强度: 0.37
- 拉伸强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 2.48
- 硬度: 93.0
- 热变形温度 [℃]: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 93 | 93 | ASTM D785 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | at max load; ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Flexural Modulus | 2.48 GPa | 360 ksi | ASTM D790 |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |