- 熔体流动速率 [g/10min]: 10.0
- 缺口冲击强度: 0.214
- 弯曲模量 [MPa]: 5.86
- 硬度: 100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Melt Flow | 10 - 20 g/10 min | 10 - 20 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength at Break | 44.8 MPa | 6500 psi | at max load; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | at max load; ASTM D638 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Izod Impact, Notched | 0.214 J/cm | 0.400 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.14 J/cm | 4.00 ft-lb/in | ASTM D256 |
| Gardner Impact | 0.678 J | 0.500 ft-lb | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |