- 熔体流动速率 [g/10min]: 6.0
- 缺口冲击强度: 0.518
- 拉伸强度 [MPa]: 54.99
- 弯曲模量 [MPa]: 3.17
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | ASTM D792 |
| Melt Flow | 6.0 - 8.0 g/10 min @Temperature 230 °C | 6.0 - 8.0 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 54.99 MPa | 7975 psi | 2 in/min; ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Strength | 90.976 MPa | 13195 psi | ASTM D790 |
| Flexural Modulus | 3.17 GPa | 460 ksi | ASTM D790 |
| Izod Impact, Notched | 0.518 J/cm | 0.970 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C | 254 °F | ASTM D648 |