- 熔体流动速率 [g/10min]: 7.0
- 缺口冲击强度: 0.427
- 拉伸强度 [MPa]: 40.0
- 弯曲模量 [MPa]: 2.41
- 硬度: 90.0
- 热变形温度 [℃]: 138.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ASTM D792 |
| Melt Flow | 7.0 - 10 g/10 min @Temperature 230 °C | 7.0 - 10 g/10 min @Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 2 in/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.1 °C | 205 °F | ASTM D648 |