- 熔体流动速率 [g/10min]: 7.0
- 缺口冲击强度: 0.294
- 拉伸强度 [MPa]: 22.5
- 弯曲模量 [MPa]: 3.40
- 热变形温度 [℃]: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 - 1.25 g/cc | 1.20 - 1.25 g/cc | ASTM D792 |
| Melt Flow | 7.0 - 10 g/10 min @Temperature 230 °C | 7.0 - 10 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | >= 80 | >= 80 | ASTM D785 |
| Tensile Strength, Yield | >= 22.5 MPa | >= 3270 psi | 2 in/min; ASTM D638 |
| Elongation at Break | >= 6.0 % | >= 6.0 % | ASTM D638 |
| Flexural Modulus | >= 3.40 GPa | >= 493 ksi | ASTM D790 |
| Izod Impact, Notched | >= 0.294 J/cm | >= 0.550 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 120 °C | >= 248 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 90.0 °C | >= 194 °F | ASTM D648 |