- 熔体流动速率 [g/10min]: 30.0
- 缺口冲击强度: 0.747
- 拉伸强度 [MPa]: 29.6
- 弯曲模量 [MPa]: 1.45
- 热变形温度 [℃]: 114.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 30 - 35 g/10 min | 30 - 35 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 29.6 MPa | 4290 psi | 2 in/min; ASTM D638 |
| Elongation at Break | 45 % | 45 % | ASTM D638 |
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | ASTM D256 |
| Gardner Impact | 2.26 J @Temperature -28.9 °C | 1.67 ft-lb @Temperature -20.0 °F | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |