- 缺口冲击强度: 3.2
- 拉伸强度 [MPa]: 21.0
- 弯曲模量 [MPa]: 0.690
- 热变形温度 [℃]: 110.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Index of Compound | 25 g/10 min @Load 2.16 kg, Temperature 230 °C | 25 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | 50 mm/min, type I bar; ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | 50 mm/min, type I bar; ASTM D638 |
| Elongation at Yield | 10 % | 10 % | 50 mm/min, type I bar; ASTM D638 |
| Flexural Modulus | 0.690 GPa | 100 ksi | 70°C, 1.3 mm/min, 50 mm span, method 1, tangent; ASTM D790 |
| 2.10 GPa | 305 ksi | 1.3 mm/min, 50 mm span, method 1, tangent; ASTM D790 | |
| 4.30 GPa @Temperature -30.0 °C | 624 ksi @Temperature -22.0 °F | 1.3 mm/min, 50 mm span, method 1, tangent; ASTM D790 | |
| Izod Impact, Notched | 3.20 J/cm | 5.99 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |