- 熔体流动速率 [g/10min]: 4.5
- 缺口冲击强度: 0.801
- 拉伸强度 [MPa]: 26.5
- 弯曲模量 [MPa]: 0.931
- 硬度: 80.0
- 热变形温度 [℃]: 105.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.890 - 0.910 g/cc | 0.890 - 0.910 g/cc | ASTM D792 |
| Melt Flow | 4.5 - 7.5 g/10 min @Temperature 230 °C | 4.5 - 7.5 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength, Yield | 26.5 MPa | 3840 psi | ASTM D638 |
| Elongation at Break | 300 % | 300 % | ASTM D638 |
| Flexural Strength | 29.0 MPa | 4210 psi | ASTM D790 |
| Flexural Modulus | 0.931 GPa | 135 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |