- 熔体流动速率 [g/10min]: 20.0
- 缺口冲击强度: 6.0
- 拉伸强度 [MPa]: 18.0
- 弯曲模量 [MPa]: 0.760
- 热变形温度 [℃]: 100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.905 g/cc | 0.905 g/cc | ASTM D792 |
| Melt Flow | 20 g/10 min @Temperature 230 °C | 20 g/10 min @Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
| Elongation at Yield | 37 % | 37 % | |
| Flexural Strength | 18.0 MPa | 2610 psi | |
| Flexural Modulus | 0.760 GPa | 110 ksi | ASTM D790 |
| Izod Impact, Notched | 6.00 J/cm | 11.2 ft-lb/in | ASTM D256 |
| Falling Dart Impact | 5.10 J @Thickness 1.78 mm, Temperature -30.0 °C | 3.76 ft-lb @Thickness 0.0701 in, Temperature -22.0 °F | Pass |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |