- 熔体流动速率 [g/10min]: 16.0
- 缺口冲击强度: 1.33
- 拉伸强度 [MPa]: 21.0
- 弯曲模量 [MPa]: 0.910
- 硬度: 85.0
- 热变形温度 [℃]: 84.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Flow | 16 - 24 g/10 min @Temperature 230 °C | 16 - 24 g/10 min @Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 250 % | 250 % | ASTM D638 |
| Elongation at Yield | 15 % | 15 % | ASTM D 638 |
| Flexural Modulus | 0.910 GPa | 132 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.01 J/cm | 15.0 ft-lb/in | -20°F; ASTM D256 |
| Gardner Impact | 3.39 J @Temperature -28.9 °C | 2.50 ft-lb @Temperature -20.0 °F | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |