- 熔体流动速率 [g/10min]: 17.0
- 缺口冲击强度: 1.07
- 拉伸强度 [MPa]: 21.0
- 弯曲模量 [MPa]: 1.00
- 热变形温度 [℃]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.902 g/cc | 0.902 g/cc | ASTM D792 |
| Melt Flow | 17 - 23 g/10 min @Load 2.16 kg, Temperature 230 °C | 17 - 23 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Flexural Modulus | 1.00 - 1.14 GPa | 145 - 165 ksi | tangent; ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.2 J/cm | 21.0 ft-lb/in | ASTM D256 |
| Gardner Impact | 13.6 J | 10.0 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |